588-10K

Overview

588-10K is a hydraulic-cement-based, precision, non-shrink, load-bearing grout designed to transfer load effectively and safely, ensuring long service time of the grouted item. It is a non-corrosive, non-metallic, mineral-based precision grout, developed to have high initial and ultimate flexural and compressive strengths. It can be mixed quickly as needed on the jobsite. 588-10K offers exceptional workability and is easily placed by pouring or pumping. The product is designed to give non-shrink performance under various conditions for both interior and exterior applications.

SCHEDULE A MEETING

REQUEST PRODUCT LITERATURE

LOCATE A DISTRIBUTOR

Sustainability

Technical Literature

Data Sheets

RESOURCES

Cold Weather Guideline: Repair Mortars and Non-Shrink Grouts

Specs & Details

Guide Specification

Guide Specification

Product Data Sheet

03 62 13

No. 380

588-10K
Non-Shrink, Non-Ferrous, Mineral-Aggregate-Based Precision Grout

DESCRIPTION

USES

588-10K is designed for precision grouting of machinery and equipment base plates, windmill turbines, generators, rolling mills, compressors, or similar types of machinery. 588-10K is also designed for grouting soleplates, bridge seats, precast columns and beams, steel column pads, precast beams, and segmental bridge construction. 588-10K can also be used for anchoring of guardrails, signposts, bridge seats, anchor bolts, guide wires, and dowels.

FEATURES/BENEFITS

May be mixed to plastic, flowable, and fluid consistencies for easy application.
Very high compressive and flexural strengths.
High modulus to ensure proper load transfer.
Non-shrink ensures proper load transfer.
Quickly and easily placed by pouring or pumping.
Resists heat up to 600˚ F (315.6° C).
Resists many chemicals, including oils, petroleum products, solvents, and mild caustic alkalis.
May be extended up to 50% by weight.
No added chloride or gypsum.

PACKAGING

50 Lb. (22.7 Kg) Poly-Lined Bags

YIELD

Each bag yields 0.43 – 0.64 ft.³ (0.012 m³ – 0.018 m³) of in-place grout using the median water ratio level, dependent upon rate of extension.

Coverage Calculator

SHELF LIFE

18 months from date of manufacture when stored indoors on pallets in a dry, cool area. Do not store product outside.

SPECIFICATIONS/STANDARDS

ASTM C 1107
Corps of Engineers Specification: CRD-C 621
USDA Accepted

APPLICATION

Grouting application shall be performed in accordance to American Concrete Institute (ACI) 351.1R: Grouting Between Foundations and Bases for Support of Equipment and Machinery and other applicable industry standard practices.

Surface Preparation … All grout contact surfaces must be free of oil, grease, scale, penetrating sealers, or all other types of contaminates that will interfere with the bond. Mechanically roughen or high-pressure water-jet the existing concrete substrate. Surface must be rough and profiled, but generally level. Grouting area must be saturated with water 12 – 24 hours prior to grouting. Remove all excess water before placing grout.

Forming … Forming method must provide for rapid, continuous grout placement. For pouring, allow a minimum clearance of 3″ (76.2 mm) for entry and 6″ (152.4 mm) minimum grout “head.” Forming must also provide for venting to avoid entrapment of air. Provide 1/2″ (12.7 mm) minimum form clearance on all sides and 1″ (25.4 mm) clearance for head. Ensure form is well sealed and an appropriate form release agent has been applied for that type of form.

Mixing … Small quantities of 588-10K may be hand-mixed in a concrete mixing pan until lump-free. For large quantities and continuous pours, mix using a mortar mixer with rubber-tipped blades or appropriate grout pump for a minimum of three minutes or until lump-free and uniform. Use the minimum water required to produce desired placement consistency. Use 6.5 pt. (3.07 L) of water per bag for plastic consistency; 7.25 pt. (3.43 L) for medium flow (pourable), and 8.25 pt. (3.9 L) for high flow. Mix in two steps: add 2/3 of water requirement, then add grout. After partial mixing, add remainder of water for desired consistency. Thoroughly mix total quantity for 2 – 3 minutes. Do not mix more than can be placed in 15 minutes at 75˚ F (23.9°). Do not re-temper.

Placement … 588-10K is easily placed by pouring or pumping and compaction can be accomplished by rodding or tapping. Place grout on one side, flowing to opposite and adjacent sides, to avoid entrapment of air. When necessary, provide vent holes. Grout head and excess grout may be removed after initial set. W. R. MEADOWS recommends the Ventures ToughTek P30 and P30ht Rotor Stator Pump (https://ventureseq.com/) combination for pump applications. The minimum thickness is project specific depending on the load bearing requirements as determined by the specifying engineer. To achieve proper flow properties for typical installations, a minimum 1/2″ (25.4 mm) is recommended.

Curing … Immediately following application, cure 588-10K using a suitable curing compound from W. R. MEADOWS or in accordance with ACI 308. The 2200-WHITE series or 1100 series from W. R. MEADOWS are recommended. When conditions exist for rapid early water loss, the use of EVAPRE_{_™}from W. R. MEADOWS is also recommended.

PRECAUTIONS

Do not use as a repair mortar. (Please contact W. R. MEADOWS for specific repair mortar recommendations.) Do not pre-mix in a ready-mix truck, either at batching plant or onsite.

TECHNICAL DATA

The following data was determined using the water amount for desired consistency as stated below per bag at 75˚ F (23˚ C).

Consistency per ASTM C827-95a	Plastic	Flowable	Fluid
Mix Ratio per 50 lb. (22.7 kg) bag	6.5 Pints (3.07 L)	7.25 Pints (3.43 L)	8.25 Pints (3.9 L)
Flow per ASTM C230-90 5 Drops/Flow Table	110%	130%
Flow per ASTM C939-94a Flow Cone			26s
SET TIME per ASTM C191-92
Initial Set	1 hr.	3 hrs.	5 hrs.
Final Set	3 hrs.	5 hrs.	7 hrs.
EXPANSION Age: 24 hours 3 days 7 days 28 days	0.13% 0.16% 0.17% 0.17%	0.10% 0.13% 0.13% 0.14%	0.02% 0.04% 0.05% 0.06%
SHRINKAGE %	NONE	NONE	NONE
COMPRESSIVE STRENGTH
AGE 1 day 3 days 7 days 28 days	psi (MPa) 5,500 (38) 6,500 (45) 7,500 (52) 11,000 (75)	psi (MPa) 4,500 (31) 5,500 (38) 6,500 (45) 9,200 (63)	psi (MPa) 3,500 (24) 4,500 (31) 5,500 (38) 8,200 (56)
All technical data is typical information, but will vary due to testing methods, conditions, procedures, batching variations, and raw materials variances.

588-10K